Aykut-Yetkiner, ArzuCandan, UmitErsin, NazanEronat, CemalBelli, SemaOzcan, Mutlu2020-03-262020-03-2620150169-42431568-5616https://dx.doi.org/10.1080/01694243.2015.1004507https://hdl.handle.net/20.500.12395/32028This study evaluated the effect of 2% chlorhexidine gluconate-based cavity disinfectant (CHX) on the microtensile bond strength (mu TBS) of glass ionomer, resin-modified glass ionomer and packable resin composite to sound and caries-affected dentin. Sound and occlusal caries-affected human third molars (N = 36, n = 3 per group) were randomly divided into three experimental groups to receive one of the following restorative materials. (a) Glass ionomer (Ketac Molar, 3M ESPE; GI), (b) resin-modified glass ionomer (Vitremer, 3M ESPE; RMGI) and (c) packable resin composite (Surefil, Dentsply; PRC) with a bonding agent (Prime Bond NT, Dentsply De Trey). Caries was removed using a caries-detecting dye (Caries Detector, Kuraray Medical Ltd.) and flat dentin surfaces were achieved by finishing up to 1200-grit silicon carbide abrasive. Half of the teeth in each group received 2% CHX (Consepsis, Ultradent). Dentin surfaces were built-up with the respective materials incrementally and were sectioned with a slow-speed saw into multiple beams. The beams were subjected to mu TBS test (0.5mm/min) in a Universal Testing Machine. The data were analysed using two-way analysis of variance and Tukey's tests. For each restorative material, mu TBS results were not affected by the application of CHX (p > 0.05) on both sound and caries-affected dentin (p > 0.05). PRC in combination with the corresponding bonding agent showed significantly higher results (p < 0.05) than those of GI and RMGI, on sound and caries-affected teeth, respectively. Cohesive failure in dentin was not observed in any of the groups. The use of 2% chlorhexidine-based cavity disinfectant did not impair the adhesion of the restorative materials tested to either sound or caries-affected dentin.en10.1080/01694243.2015.1004507info:eu-repo/semantics/openAccessmicrotensile bond strengthcavity disinfectantchlorhexidineglass ionomer cementcomposite resinArticle291211691177Q2WOS:000352351200001Q3