Kara, Haluk BarisOzturk, A. NilgunAykent, FilizKoc, OzlemOzturk, Bora2020-03-262020-03-2620110268-89211435-604Xhttps://dx.doi.org/10.1007/s10103-010-0806-9https://hdl.handle.net/20.500.12395/26905The aim of this study was to evaluate the influence of different surface treatments (air abrasion, acid etching, and laser irradiation) on the surface roughness and bond strength of a low fusing ceramic. Thirty-six discs of low fusing ceramic (Finesse, Ceramco) were prepared (10 mm in diameter and 2 mm in thickness) according to the manufacturer's instructions. Specimens were divided into three groups (n = 12), and the following treatments were performed: Air abrasion with alumina particles (50 mu m), acid etching with 5% HF and Nd:YAG laser irradiation (distance: 1 mm, 100 mJ, 20 Hz, 2 W, and 141.54 J/cm(2)). Following determination of surface roughness (R-a) by profilometry, specimens were examined with scanning electron microscopy (SEM). The luting cement (Clearfil Esthetic Cement) was bonded to the ceramic specimens using Teflon tubes. After 24 h of water storage, shear bond strength test was performed using a universal testing machine at a crosshead speed of 1 mm/min. The data were analyzed with two-way analysis of variance (ANOVA) and Tukey HSD tests (alpha = .05). Two-way ANOVA indicated that surface roughness was significantly affected by surface treatments (p < .001). Tukey honestly significant difference (HSD) indicated that the air abrasion group had a significantly higher mean value (p < .05) than the other groups. Shear bond strength was significantly affected by surface treatments (p < .001). Tukey HSD indicated that the air abrasion group had a significantly higher mean value (p < .05) than the other groups. No significant difference was found between the acid-etching and laser-irradiation groups (p > .05). The SEM image of the laser irradiation surface appeared to be relatively smooth as compared to the images of other the groups. Air abrasion of low-fusing porcelain surfaces was effective in improving the bond strength as compared to the acid-etching and laser-irradiation methods.en10.1007/s10103-010-0806-9info:eu-repo/semantics/closedAccessBond strengthLuting cementsSurface treatmentCeramicLaserArticle26559960420585967Q2WOS:000293650000007Q2