Yazar "Durmusoglu, Senol" seçeneğine göre listele
Listeleniyor 1 - 4 / 4
Sayfa Başına Sonuç
Sıralama seçenekleri
Öğe Fabrication and characterization of bismuth oxide-holmia nanofibers and nanoceramics(ELSEVIER SCIENCE BV, 2013) Aytimur, Arda; Kocyigit, Serhat; Uslu, Ibrahim; Durmusoglu, Senol; Akdemir, AhmetIn this article, a novel and simple method to produce both boron doped and undoped holmia stabilized bismuth oxide nanoceramic materials has been put forward. Boron doped and undoped poly ( vinyl alcohol)/bismuth-holmia acetate nanofibers were produced using the electrospinning technique and were calcined at 850 degrees C afterward in order to obtain nanopowder. The characteristics of the nanofibers were investigated with FT-IR, XRD, and SEM. XRD analyses showed that boron undoped holmia stabilized bismuth oxide nanopowders have the face-centered cubic structure (delta-phase), and that the incorporation of boron atoms into the composite prevents the nucleus formation and turns the structure into a more amorphous glassy form. The SEM micrographs of the fibers showed that the addition of boron results in the formation of cross-linked bright-surfaced fibers. The average fiber diameters for electrospun boron doped and undoped PVA/Bi-Ho acetate nanofibers were calculated using the ImageJ software as 102 nm and 171 nm, respectively. (C) 2012 Elsevier B.V. All rights reserved.Öğe Polymer-derived yttria stabilized bismuth oxide nanocrystalline ceramics(ELSEVIER SCI LTD, 2014) Aytimur, Arda; Uslu, Ibrahim; Durmusoglu, Senol; Akdemir, AhmetBoron doped and undoped Bi2O3-Y2O3 nanofibers were synthesized by the electrospinning method. The nanofibers were then calcined to obtain nanocrystalline ceramics. The synthesized nanofibers and nanocrystalline ceramics were characterized using XRD, FT-IR, SEM and XPS. According to the XRD results the undoped Bi2O3-Y2O3 nanocrystalline ceramic has a face-centered cubic structure. The XPS results show that nanocrystalline ceramics were pure Bi2O3, and there were no peaks related to either bivalent or tetravalent or pentavalent states in Bi2O3. The XPS results also show that the crystallinity of the boron doped nanocrystalline ceramic was decreased because of the network former property of the boron. The average fiber diameters for electrospun boron doped and undoped PVA/Bi-Y acetate nanofibers were calculated as 179 nm and 96 nm, respectively. The SEM micrographs of the nanocrystalline ceramics show that the undoped Bi2O3-Y2O3 ceramic has needle-like crystalline structure. However, the crystallinity of the boron doped Bi2O3-Y2O3 ceramic decreased because of boron doping. (C) 2014 Elsevier Ltd and Techna Group S.r.l. All rights reserved.Öğe Synthesis and characterization of boron-doped Bi2O3-La2O3 fiber derived nanocomposite precursor(SPRINGER, 2011) Durmusoglu, Senol; Uslu, Ibrahim; Tunc, Tuncay; Keskin, Selda; Aytimur, Arda; Akdemir, AhmetBoron doped poly(vinyl) alcohol/ bismuth - lanthanum acetate (PVA/Bi-La) nanofibers were prepared by electrospinning using PVA as a precursor. The effect of boron doping was investigated in terms of solution properties, morphological changes and thermal characteristics. The fibers were characterized by FT-IR, XRD, SEM and BET. The addition of boron did not only increase the thermal stability of the fibers, but also their diameters, which yielded stronger fibers. XRD analyses showed that boron doping increased the peak intensities and indicated that the boron doping enhanced the crystallite size. Moreover, no shifts were noticed in diffraction angles for boron doped and undoped samples. Therefore, boron doping did not significantly alter the lattice spacing. The SEM micrograph of the fibers showed that the addition of boron resulted in the formation of cross linked bright surfaced fibers. Also, grain diameters of boron doped and undoped nanocrystalline sintered powders were measured as 170 nm and 120 nm respectively. The BET results show that boron undoped and doped Bi2O3-La2O3 nanocrystalline powder ceramic structures sintered at 800 A degrees C have surface areas of 20.44 m(2)/g and 12.93 m(2)/g, respectively.Öğe Synthesis and characterization of boron-doped bismuth oxide-erbium oxide fiber derived nanocomposite precursor(SAGE PUBLICATIONS LTD, 2014) Aytimur, Arda; Kocyigit, Serhat; Uslu, Ibrahim; Durmusoglu, Senol; Akdemir, AhmetIn this study, boron doped and undoped Bi2O3-Er2O3 nanocomposite fibers were produced via electrospinning technique. Obtained fibers were turned into ceramics via calcination process. Obtained nanocomposite fibers and ceramics were characterized by Fourier transform infrared, x-ray diffraction, and scanning electron microscopy techniques. X-ray diffraction results show that boron undoped Bi2O3-Er2O ceramic consisted of face-centered cubic Bi2O3-Er2O phase. However, boron doped Bi2O3-Er2O ceramic consisted of orthorhombic phase. Crystallite sizes of the ceramics were evaluated using Scherrer's equation. Crystallite sizes of boron doped and undoped ceramics were calculated as 50 and 17 nm, respectively. The average fiber diameters for boron doped and undoped poly vinyl alcohol/Bi-Er acetate nanofibers were calculated as 79 nm and 96 nm, respectively. The Brunauer Emmett teller results show that boron undoped and doped Bi2O3-Er2O nanocrystalline powder ceramic structures sintered at 800 degrees C have surface area of 20.44 and 12.93 m(2)/g, respectively.