Yazar "Gunes, Aydin." seçeneğine göre listele
Listeleniyor 1 - 2 / 2
Sayfa Başına Sonuç
Sıralama seçenekleri
Öğe Experimental study and analysis of machinability characteristics of metal matrix composites during drilling(ELSEVIER SCI LTD, 2019) Salur, Emin.; Aslan, Abdullah.; Kuntoglu, Mustafa.; Gunes, Aydin.; Sahin, Omer Sinan.In this study, the metal matrix composite materials were produced by hot press with various production parameters. The drilling experiments were performed on computer numerical control vertical machining centre without cutting fluid. Analysis of variance (ANOVA) was carried out in order to determine the effects of the production parameters on thrust force and surface roughness of metal matrix composites drilled with different feed rate. The effect of production parameters such as temperature, pressure and reinforcement ratio were investigated, and their effects were presented. The optimal level for each production parameters was determined by 'Maximize the S/N ratio approach with a Taguchi design'. The test results revealed that the reinforcement ratio was the main factor affecting the surface roughness of the metal matrix composites for both feed rate. However, same singularity was not matter on thrust force due to close contribution rates of production parameters and high error rates of analysis. In literature, an increase on the thrust force and the surface roughness values was reported as the feed rate increased during machining. Nevertheless, in our MMCs system, the thrust force and the surface roughness values were in tendency of declination / as the feed rate increased which makes this study more novel research.Öğe The mechanical properties of composite materials recycled from waste metallic chips under different pressures(SPRINGER, 2019) Aslan, Abdullah.; Salur, Emin.; Gunes, Aydin.; Sahin, Omer Sinan.; Karadag, Hakan Burak.; Akdemir, Ahmet.The purpose of this study is to produce composite materials by utilizing the waste metallic chips. In this context, the metal matrix composite materials (MMCs) were produced at different production pressures and the effects of the different pressures on mechanical properties of MMCs were investigated. In the present investigation, spheroidal graphite cast iron (GGG-40) was used as reinforcement material in bronze (CuSn10) matrix system. The MMCs were produced by hot press with 20 wt% GGG-40 reinforcement ratio. The total time required for the production of one specimen was selected as 25 min and temperature was settled at 400 degrees C. In order to determine mechanical properties and consolidation mechanism of MMCs, Brinell and micro-Vickers hardness, porosity, compression and X-ray diffraction tests were conducted. In addition, microstructure views were examined to determine the consolidation quality of metallic chips. According to experimental results, it was observed that waste metallic chips can be successfully recycled into MMC final parts with approximately 40% porosity and almost 100% strength and 150% hardness with respect to bulk CuSn10 materials. Most of the presented studies in the literature present information about properties of MMCs fabricated by conventional production methods. However, no available data are found about the recycling of bronze-based MMCs which make this study more original. It is also shown in this study that waste metallic chips can be utilized by proposed recycling methodology, which is environmentally friendly in comparison with conventional recycling methods producing harmful gases for earth atmosphere.