Yazar "Koyuturk, AE" seçeneğine göre listele
Listeleniyor 1 - 4 / 4
Sayfa Başına Sonuç
Sıralama seçenekleri
Öğe Effect of desensitizers on the bond strength of a self-etching adhesive system to caries-affected dentin on the gingival wall(OPERATIVE DENTISTRY INC, 2005) Sengun, A; Koyuturk, AE; Sener, Y; Ozer, FA self-etching dentin adhesive was evaluated for its ability to bond to caries-affected and sound dentin after applying three desensitizers to the gingival walls. Sixty extracted human molars, with approximal dentin caries, were cut horizontally on the long axis of the tooth through caries-affected gingival walls. Carious dentin was removed with SiC paper by means of a caries detector to expose caries-affected dentin. The molars were randomly assigned to four groups: control and three experimental groups-Micro Prime, Glauma Desentizer and Cervitec. Desensitizers were applied to the dentinal surfaces according to manufacturers' instructions. A resin composite was bonded to both the caries-affected and sound dentin of each tooth using a bonding system and plastic rings. The restoration was debonded by shear bond strength. The application of Micro Prime and Gluma Desensitizer to caries-affected dentin did not show any effect on bond strength testing. However, Cervitec caused a decrease in bond strength to caries-affected dentin. The effect of desensitizers on the bond strength of the self-etch bonding agent to caries-affected dentin changed according to the chemical composition of the materials. Desensitizer application on sound dentin is recommended with self-etch bonding systems.Öğe The effect of head rotation on cephalometric radiographs(OXFORD UNIV PRESS, 2005) Malkoc, S; Sari, Z; Usumez, S; Koyuturk, AE[Abstract not Available]Öğe Effects of chlorhexidine and povidone-iodine mouth rinses on the bond strength of an orthodontic composite(E H ANGLE EDUCATION RESEARCH FOUNDATION, INC, 2005) Demir, A; Malkoc, S; Sengun, A; Koyuturk, AE; Sener, YThe purpose of this study was to determine whether the application of two antibacterial mouth rinses to etched and unetched enamel affects the shear bond strength (SBS) of an orthodontic composite resin. Eighty-five lower human incisors were divided into five groups, ie, group 1: control group, no mouth rinse was used; groups 2 and 3: mouth rinses were applied to the intact enamel surface before etching; groups 4 and 5: mouth rinses were applied to the etched enamel. A bonding agent and a composite resin were applied to the teeth surface. For shear bond testing, the specimens were mounted in a universal testing machine, and an apparatus attached to a compression load cell was applied to each specimen until failure occurred. The data were analyzed using analysis of variance and Tukey honestly significance tests. Fracture modes were analyzed by Mann-Whitney U-test. There was no statistically significant difference between the SBS values of group 1 (31.64 +/-- 3.62 MPa) and group 4-five experimental applications (P >= .05). However, the SBS value of group 3 (36.56 +/- 5.95 MPa) was significantly larger than those of group 4 (30.00 +/- 4.97 MPa) and group 5 (30.26 +/- 7.30 MPa). In addition, no significant differences were observed between group 1 and groups 2 (34.33 +/- 7.26 MPa) and 3 (36.56 +/- 5.95 MPa) (P >= .05). Because the application of chlorhexidine and povidone-iodine before acid etching did not cause any decrease in bond strength, it is advisable for use under the orthodontic resin composite to obtain an antibacterial effect or to prevent the risk of bacteremia.Öğe Shear bond strengths of self-etching adhesives to caries-affected dentin on the gingival wall(JAPANESE SOC DENTAL MATERIALS DEVICES, 2006) Koyuturk, AE; Sengun, A; Ozer, F; Sener, Y; Gokalp, AThe purpose of this study was to evaluate the bonding ability of five current self-etching adhesives to caries-affected dentin on the gingival wall. Seventy extracted human molars with approximal dentin caries were employed in this study. In order to obtain caries-affected dentin on the gingival wall, grinding was performed under running water. Following which, specimens mounted in acrylic blocks and composite resins of the bonding systems were bonded to dentin with plastic rings and then debonded by shear bond strength. With Clearfil SE Bond, bonding to caries-affected dentin showed the highest bond strength. With Optibond Solo Plus Self-Etch, bonding to caries-affected dentin showed higher shear bond strength than AQ Bond, Tyrian SPE & One-Step Plus, and Prompt-L-Pop (p<0.05). Further, the bond strengths of Clearfil SE Bond and Optibond Solo Plus Self-Etch to sound dentin were higher than those of Prompt-L-Pop, AQ Bond, and Tyrian SPE & One-Step Plus (p<0.05). In conclusion, besides micromechanical interlocking through hybrid layer formation, bond strength of self-etch adhesives to dentin may be increased from additional chemical interaction between the functional monomer and residual hydroxyapatite. The results of this study confirmed that differences in bond strength among self-etching adhesives to both caries-affected and sound dentin were due to chemical composition rather than acidity.