Resiprokal Hareket İle Kullanılan Isıl İşlem Görmüş Tek Eğe Nikel Titanyum Sistemlerin Vücut Sıcaklığında Döngüsel Yorgunluk Dirençlerinin Karşılaştırılması

Basit Öğe Kaydı
dc.authorid0000-0002-1721-1838en_US
dc.authorid0000-0003-3286-069Xen_US
dc.authorid0000-0001-8990-4847en_US
dc.authorid0000-0001-8899-2152en_US
dc.authorid0000-0002-6834-4307en_US
dc.contributor.authorBaş, Gözde
dc.contributor.authorYüzgüleç, Elçin
dc.contributor.authorKeskin, Cangül
dc.contributor.authorİnan, Uğur
dc.contributor.authorKeleş, Ali
dc.date.accessioned2023-01-18T08:55:08Z
dc.date.available2023-01-18T08:55:08Z
dc.date.issued2021en_US
dc.departmentBaşka Kurumen_US
dc.description.abstractAmaç: Bu çalışmanın amacı WaveOne Gold, Reciproc Blue ve North Profa RC Blue nikel titanyum (NiTi) tek eğe döner sistemlerin vücut sıcaklığında döngüsel yorgunluğa bağlı kırılma dirençlerinin ve faz değişim derecelerinin karşılaştırılmasıdır. Gereç ve Yöntemler: Bu çalışmada 12 WaveOne Gold, 12 Reciproc Blue ve 12 North Profa RC Blue döner eğe sistem NiTi eğeleri kullanıldı. Tüm eğeler, 60°’lik kurvatür açısına, 5 mm kurvatür yarıçapına ve 1.4 mm kanal iç çapına sahip seramik yapay kanal içeren statik döngüsel yorgunluk deney düzeneğinde 37°C’de kırılıncaya kadar kullanıldı. Eğelerin kırılma zamanı dijital kronometre ile kaydedildi ve kırılıncaya kadarki tur sayıları hesaplandı. Normal dağılım göstermediği saptanan veriler Kruskal-Wallis H testi ile analiz edildi. Tahmini sağlam kalma oranının belirlenmesi için Weibull analizi yapıldı. Bulgular: North Profa RC Blue grubu ile Reciproc Blue grubu arasında ve Reciproc Blue grubu ile WaveOne Gold grubu arasında döngüsel yorgunluk direnci bakımından istatistiksel olarak anlamlı bir fark görülmedi (p>0.05). North Profa RC Blue eğelerin döngüsel yorgunluk direnci WaveOne Gold eğelerden istatistiksel olarak anlamlı derecede yüksek bulundu (p<0.05). Kırık yüzeylerden alınan SEM görüntüleri incelenerek aletlerin döngüsel yorgunluk sonucunda kırıldığı doğrulandı. Sonuç: Bu çalışmada, North Profa RC Blue ve Reciproc Blue eğelerin döngüsel yorgunluk dirençleri arasında fark bulunmazken, WaveOne Gold eğelerin döngüsel yorgunluk direnci North Profa RC Blue eğelerden daha düşük bulundu.en_US
dc.description.abstractBackground: The aim of this study was to compare the phase transformation temperatures and cyclic fatigue resistances of WaveOne Gold, Reciproc Blue and North Profa RC Blue nickel titanium (NiTi) instruments at body temperature. Methods: In this study 12 WaveOne Gold, 12 Reciproc Blue and 12 North Profa RC Blue rotary system NiTi files were used. All instruments were used in a static cyclic fatigue testing device, which has an artificial ceramic canal with a radius of curvature of 5 mm, an angle of curvature of 60° and a 1,4 mm inner diameter at 37°C until the fracture occurred. The time to failure of the files was recorded using a digital chronometer and the number of cycles to failure of files were calculated. Non-normally distributed data were analyzed by Kruskal-Wallis H test. Weibull analysis was performed to determine the estimated survival rate. Results: There was no statistically significant difference between the North Profa RC Blue group and the Reciproc Blue group, and between the Reciproc Blue group and the WaveOne Gold group in terms of cyclic fatigue resistance (p>0.05). Cyclic fatigue resistance of North Profa RC Blue group was statistically higher than WaveOne Gold group (p<0.05). SEM images taken from fractured surfaces confirmed that the instrument fracture occurred as the result of cyclic fatigue. Conclusion: In this study, no difference was found between the cyclic fatigue resistances of North Profa RC Blue and Reciproc Blue instruments, while the cyclic fatigue resistance of the WaveOne Gold instruments was found to be lower than the North Profa RC Blue.en_US
dc.identifier.citationBaş, G., Yüzgüleç, E., Keskin, C., İnan, U., Keleş, A., (2021). Resiprokal Hareket İle Kullanılan Isıl İşlem Görmüş Tek Eğe Nikel Titanyum Sistemlerin Vücut Sıcaklığında Döngüsel Yorgunluk Dirençlerinin Karşılaştırılması. Selçuk Üniversitesi Diş Hekimliği Fakültesi Dergisi, 8 (3), 658-664. Doi: 10.15311/selcukdentj.760048en_US
dc.identifier.doi10.15311/selcukdentj.760048en_US
dc.identifier.endpage664en_US
dc.identifier.issn2148-7529en_US
dc.identifier.issue3en_US
dc.identifier.startpage658en_US
dc.identifier.urihttps://hdl.handle.net/20.500.12395/44900
dc.identifier.volume8en_US
dc.language.isotren_US
dc.publisherSelçuk Üniversitesien_US
dc.relation.ispartofSelçuk Üniversitesi Diş Hekimliği Fakültesi Dergisien_US
dc.relation.publicationcategoryMakale - Uluslararası Hakemli Dergi - Başka Kurum Yazarıen_US
dc.rightsinfo:eu-repo/semantics/openAccessen_US
dc.selcuk20240510_oaigen_US
dc.subjectNorth Profaen_US
dc.subjectReciproc Blueen_US
dc.subjectSeramik kanalen_US
dc.subjectTaramalı elektron mikroskobuen_US
dc.subjectWaveOne Golden_US
dc.subjectCeramic canalen_US
dc.subjectNorth Profaen_US
dc.subjectScanning electron microscopeen_US
dc.subjectWaveOne Golden_US
dc.titleResiprokal Hareket İle Kullanılan Isıl İşlem Görmüş Tek Eğe Nikel Titanyum Sistemlerin Vücut Sıcaklığında Döngüsel Yorgunluk Dirençlerinin Karşılaştırılmasıen_US
dc.title.alternativeComparison of Cyclic Fatigue Resistance of Thermal Treated Nickel Titanium Single File Systems Used with Reciprocating Motion at Body Temperatureen_US
dc.typeArticleen_US

Dosyalar

Orijinal paket
Listeleniyor 1 - 1 / 1
Küçük Resim
İsim:
10.pdf
Boyut:
965.35 KB
Biçim:
Adobe Portable Document Format
Açıklama:
Makale Dosyası
İndir
Lisans paketi
Listeleniyor 1 - 1 / 1
Küçük Resim Yok
İsim:
license.txt
Boyut:
1.44 KB
Biçim:
Item-specific license agreed upon to submission
Açıklama:
İndir

Koleksiyon

Dergi Yayın Koleksiyonu