Pamuklu kumaşların buruşmazlık açısının iyileştirilmesi

dc.authorid0000-0003-2448-0937en_US
dc.contributor.advisorÖzcan, Emine
dc.contributor.authorBalcı, Selvi Merve
dc.date.accessioned2022-08-12T10:27:52Z
dc.date.available2022-08-12T10:27:52Z
dc.date.issued2021en_US
dc.date.submitted2021
dc.departmentEnstitüler, Fen Bilimleri Enstitüsü, Kimya Ana Bilim Dalıen_US
dc.description.abstractBu tez kapsamında pamuklu kumaşlarda buruşmazlık açısını iyileştirmek amacıyla, silikon yağı olarak düşük amin sayılı reaktif aminoetil aminopropil fonksiyonel polidimetilsiloksan kullanılmıştır. Emülgatör olarak literatürlerden farklı olarak ilk kez Tridesil Alkol 5 Etoksilat ve Tridesil Alkol 8 Etoksilat kullanılarak amino fonksiyonel silikon emülsiyonu hazırlanmıştır. Hazırlanan silikon emülsiyonunun pH, raf ömrü testi, kırılma indisi tayini, FT-IR spektroskopisi ve Partikül Boyut Analizi yapılmıştır. Silikon emülsiyonu yaygın olarak kullanılan pad-dry-cure metoduna göre 20g/L, 40g/L ve 60g/L olmak üzere üç farklı konsantrasyonda %100 pamuklu kumaşa uygulanmıştır. Emülsiyon uygulanan pamuklu kumaşın kurutma sıcaklığı ve süresi 120 °C 'de 5 dakika, fikse edilme sıcaklığı ve süresi ise 170°C 'de 3 dakikadır. Amino fonksiyonel silikon emülsiyonunun uygulandığı kumaşlarda kalitatif tuşe testi, FT-IR spektroskopisi, SEM analizi ve buruşmazlık açısı tayini (WRA) yapılmıştır. FT-IR spektroskopisi değerleri incelendiğinde üretilen amino fonksiyonel silikon emülsiyonunun %100 pamuklu kumaşa bağlandığı kanıtlanmıştır. SEM görüntüleri incelendiğinde pamuklu ham kumaş yüzeyi buruşuk, kıvrımlı ve sert yüzey olarak gözlemlenmiştir. Emülsiyon uygulandıktan sonra ise daha düzgün ve pürüzsüz bir yüzeyin gözlemlenmesi amino fonksiyonel silikon emülsiyonunun pamuklu kumaşa bağlandığının kanıtıdır. Pamuklu kumaşın buruşmazlık açısı tayini (WRA), üretilen silikon emülsiyonu kumaşlara uygulandıktan sonra kurutulmuş ve 170 °C 'de 3 dakika fikse edildikten sonra yapılmıştır. Buruşmazlık açısı ölçümü kumaşların atkı ve çözgü yönlerinde ayrı ayrı ölçülerek belirlenmiştir. Buruşmazlık açısı ölçümü sonucunda konsantrasyon arttıkça buruşmazlık açsının arttığı gözlemlenmiştir.en_US
dc.description.abstractIn this thesis, an emulsion was prepared by using reactive aminoethyl aminopropyl functional polydimethylsiloxane silicone oil in order to improve the wrinkle recovery angle of cotton fabrics. Different from the literatüre, amino functional silicone emulsion was prepared for the first time by using as emulsifiers Tridecyl Alcohol 5 Ethoxylate and Tridecyl Alcohol 8 Ethoxylate. The prepared silicone emulsion was performed pH, refractive index, FT IR Spectroscopy and Particle Size Analysis. The silicone emulsion was applied to 100% cotton fabric according to the commonly used pad-dry-cure method at three different concentrations; 20g/L, 40g/L and 60g/L. Applied to cotton fabric that drying temperature and time is 5 minutes at 120 °C, fixation temperature and time is 3 minutes at 170 °C. Qualitative touch test, FT IR spectroscopy, SEM analysis and wrinkle recovery angle (WRA) were performed on cotton fabric which amino functional silicone emulsions was applied. When the FT IR spectroscopy values were examined, it was proven that the amino functional silicone emulsion produced was bonded to %100 cotton fabric. When the SEM images were examined, raw cotton fabric surface was observed as wrinkled, curved and hard surface. Observing a smoother and smoother surface after the emulsion is bonded to cotton fabric. Wrinkle recovery angle (WRA) of cotton fabric was made after the silicone emulsion produced that applied to the fabric fixation temperature at 170 °C and 3 minutes. Wrinkle recovery angle measurement was determined weft and warp directions of cotton fabric measuring by separately. As a result of wrinkle recovery angle measurement was observed that wrinkle recovery angle increased as concentrations increased.en_US
dc.identifier.citationBalcı, S. M. (2021). Pamuklu kumaşların buruşmazlık açısının iyileştirilmesi. (Doktora Tezi). Selçuk Üniversitesi, Fen Bilimleri Enstitüsü, Konya.en_US
dc.identifier.urihttps://hdl.handle.net/20.500.12395/42634
dc.language.isotren_US
dc.publisherSelçuk Üniversitesi Fen Bilimleri Enstitüsüen_US
dc.relation.publicationcategoryTezen_US
dc.rightsinfo:eu-repo/semantics/openAccessen_US
dc.selcuk20240510_oaigen_US
dc.subjectBuruşmazlık açısıen_US
dc.subjectSilikon emülsiyonuen_US
dc.subjectSilikonlaren_US
dc.subjectSilicone emulsionsen_US
dc.subjectWrinkle recovery angleen_US
dc.subjectCrease-free angleen_US
dc.titlePamuklu kumaşların buruşmazlık açısının iyileştirilmesien_US
dc.title.alternativeImproving the wrinkle recovery angle of cotton fabricsen_US
dc.typeDoctoral Thesisen_US

Dosyalar

Orijinal paket
Listeleniyor 1 - 1 / 1
Yükleniyor...
Küçük Resim
İsim:
SELVİ MERVE BALCI.pdf
Boyut:
1.6 MB
Biçim:
Adobe Portable Document Format
Açıklama:
Lisans paketi
Listeleniyor 1 - 1 / 1
Küçük Resim Yok
İsim:
license.txt
Boyut:
1.44 KB
Biçim:
Item-specific license agreed upon to submission
Açıklama: