Shear-bond-strength of orthodontic brackets to aged nano-hybrid composite-resin surfaces using different surface preparation
Küçük Resim Yok
Tarih
2015
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
JAPANESE SOC DENTAL MATERIALS DEVICES
Erişim Hakkı
info:eu-repo/semantics/openAccess
Özet
The aim of this study was to evaluate the effects of different surface preparation methods on the shear bond strength (SBS) of orthodontic metal brackets to aged nano-hybrid resin composite surfaces in vitro. A total of 100 restorative composite resin discs, 6 mm in diameter and :3 mm thick, were obtained and treated with an ageing procedure. After ageing, the samples were randomly divided as follows according to surface preparation methods: (1)Control, (2)37% phosphoric acid gel, (3)Sandblasting, (4)Diamond bur, (5)Air-flow and 20 central incisor teeth were used for the control etched group. SBS test were applied on bonded metal brackets to all samples. SBS values and residual adhesives were evaluated. Analysis of variance showed a significant difference (p<0.001) between the groups. Sandblasted group had the highest SBS value (12.85 MPa) in experimental groups. The sandblasting surface treatment is recommended as an effective method of bonding orthodontic metal brackets to nano-hybrid composite resin surfaces.
Açıklama
Anahtar Kelimeler
Bracket, Shear-bond-strength, Nano-hybrid resin composite
Kaynak
DENTAL MATERIALS JOURNAL
WoS Q Değeri
Q3
Scopus Q Değeri
Q1
Cilt
34
Sayı
1