Effect of Different Surface Treatments on the Bond Strength of Lithium Disilicate Ceramic to the Zirconia Core
Küçük Resim Yok
Tarih
2016
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
MARY ANN LIEBERT, INC
Erişim Hakkı
info:eu-repo/semantics/closedAccess
Özet
Objective:The aim of this study was to evaluate the effect of different surface treatments [sandblasting, Erbium:Yttrium-Aluminium-Garnet (Er:YAG), and femtosecond lasers] on the shear bond strength (SBS) of the CAD-on technique. Background data:Although demand for all-ceramic restorations has increased, chipping remains one of the major problems for zirconia-based restorations. Materials and methods:Forty yttrium-stabilized tetragonal zirconia polycrystalline (Y-TZP) zirconia plates (IPS e.max ZirCAD, Ivoclar Vivadent) were cut, sintered (12.4 x 11.4 x 3 mm) and divided into four groups according to the surface treatments (n = 10): a control group with no surface treatment (Group C), sandblasting with 50 mu m Al2O3 (Group S), Er:YAG laser irradiation (Group E), and femtosecond laser irradiation (Group F). Also, 40 cylindrical (5mm diameter, 2mm height) lithium disilicate (IPS e.max CAD) veneer ceramics were cut and fused to all zirconia cores by a glassfusion ceramic and crystallized according to the CAD-on technique. Specimens were subjected to shear force using a universal testing machine. The load was applied at a crosshead speed of 0.5 mm/min until failure. Mean SBS (MPa) were analyzed with one way ANOVA (p < 0.05). The failed specimens were examined under a stereomicroscope at x 20 to classify the mode of failure. Results:The highest SBS was observed in Group F (36 +/- 3.31 MPa), followed by Group S (33.03 +/- 5.05 MPa), and Group C (32.52 +/- 10.15 MPa). The lowest SBS was observed in Group E (31.02 +/- 4.96 MPa), but no significant differences were found between the control and surface treated groups (p = 0.377). All the specimens showed a mixed type of failure. Conclusions: Femtosecond laser application increased the bond strength between zirconia-veneer specimens. However, the novel CAD-on technique with no surface treatment also showed high bonding strength. Thus, this technique could prevent ceramic chipping without additional surface treatments.
Açıklama
Anahtar Kelimeler
Kaynak
PHOTOMEDICINE AND LASER SURGERY
WoS Q Değeri
Q3
Scopus Q Değeri
N/A
Cilt
34
Sayı
6