Mixed-mode Fracture Toughness and Kink Formation of Woven Glass Reinforced Epoxy Composites

Küçük Resim Yok

Tarih

2009

Dergi Başlığı

Dergi ISSN

Cilt Başlığı

Yayıncı

SAGE PUBLICATIONS LTD

Erişim Hakkı

info:eu-repo/semantics/closedAccess

Özet

In this study the fracture behavior of woven glass fiber reinforced epoxy composites with trough thickness crack oriented at different angles were investigated. The composite plates consisting of five layers have a thickness of 1.2 mm. The trough cracks were formed at the center of the specimens with lengths of 5 mm, 7 mm and 9 mm. The fracture behavior of the composites, subjected to tensile loading and kink formation, were investigated. The fracture toughness of the composite specimens was determined by using both initial notch depth and the compliance method. The experimental results were presented in graphical form.

Açıklama

Anahtar Kelimeler

composite material, mixed mode fracture, kink formation, toughness

Kaynak

JOURNAL OF REINFORCED PLASTICS AND COMPOSITES

WoS Q Değeri

Q2

Scopus Q Değeri

Q1

Cilt

28

Sayı

2

Künye