Mixed-mode Fracture Toughness and Kink Formation of Woven Glass Reinforced Epoxy Composites

Basit Öğe Kaydı
dc.contributor.authorColak, Fatih M.
dc.contributor.authorDaghan, Behcet
dc.contributor.authorSahin, Oemer Sinan
dc.date.accessioned2020-03-26T17:39:16Z
dc.date.available2020-03-26T17:39:16Z
dc.date.issued2009
dc.departmentSelçuk Üniversitesien_US
dc.description.abstractIn this study the fracture behavior of woven glass fiber reinforced epoxy composites with trough thickness crack oriented at different angles were investigated. The composite plates consisting of five layers have a thickness of 1.2 mm. The trough cracks were formed at the center of the specimens with lengths of 5 mm, 7 mm and 9 mm. The fracture behavior of the composites, subjected to tensile loading and kink formation, were investigated. The fracture toughness of the composite specimens was determined by using both initial notch depth and the compliance method. The experimental results were presented in graphical form.en_US
dc.description.sponsorshipSelcuk University, TurkeySelcuk Universityen_US
dc.description.sponsorshipThis work was supported by the Coordinatorship of Scientific Research projects of Selcuk University, Turkey.en_US
dc.identifier.doi10.1177/0731684407084117en_US
dc.identifier.endpage155en_US
dc.identifier.issn0731-6844en_US
dc.identifier.issn1530-7964en_US
dc.identifier.issue2en_US
dc.identifier.scopusqualityQ1en_US
dc.identifier.startpage147en_US
dc.identifier.urihttps://dx.doi.org/10.1177/0731684407084117
dc.identifier.urihttps://hdl.handle.net/20.500.12395/23684
dc.identifier.volume28en_US
dc.identifier.wosWOS:000262443100002en_US
dc.identifier.wosqualityQ2en_US
dc.indekslendigikaynakWeb of Scienceen_US
dc.indekslendigikaynakScopusen_US
dc.language.isoenen_US
dc.publisherSAGE PUBLICATIONS LTDen_US
dc.relation.ispartofJOURNAL OF REINFORCED PLASTICS AND COMPOSITESen_US
dc.relation.publicationcategoryMakale - Uluslararası Hakemli Dergi - Kurum Öğretim Elemanıen_US
dc.rightsinfo:eu-repo/semantics/closedAccessen_US
dc.selcuk20240510_oaigen_US
dc.subjectcomposite materialen_US
dc.subjectmixed mode fractureen_US
dc.subjectkink formationen_US
dc.subjecttoughnessen_US
dc.titleMixed-mode Fracture Toughness and Kink Formation of Woven Glass Reinforced Epoxy Compositesen_US
dc.typeArticleen_US

Dosyalar

Koleksiyon

WoS İndeksli Yayınlar Koleksiyonu
Scopus İndeksli Yayınlar Koleksiyonu