Conversion Degree, Microhardness, Microleakage and Fluoride Release of Different Fissure Sealants
Yükleniyor...
Dosyalar
Tarih
2010
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
ELSEVIER
Erişim Hakkı
info:eu-repo/semantics/openAccess
Özet
The purpose of this study was to determine the degree of conversion (DC), microhardness, microleakage and fluoride release of a nano-filled resin based fissure sealant (Grandio Seal, GS) and compare it with an un-filled resin based fissure sealant (Clinpro, CL) and a glassionomer based fissure sealant (Fuji Triage, FT). Disk shaped specimens were prepared from tested fissure sealants to determine the DC, Vicker hardness (VHN) and fluoride release (FR). The DC and VHN of each material was evaluated after 24 h. The cumulative fluoride concentrations were evaluated at 1 h, 6 h, 12 h, 1, 7, 15 and 30 days. For microleakage evaluation, fissure sealants were applied to the etched and dried enamel surfaces of sound third molar teeth according to the manufacturer’s instructions (n = 10). After the thermocycling and mechanical loading procedures, microleakage assessments were carried out. Data were analyzed using oneway ANOVA followed by a post hoc Tukey test, the Kruskal Wallis and Mann–Whitney U test (p < 0.05). Results revealed differences regarding DC between all groups: FT (89%) > GS (55.02%) > CL (%51.10) (p < 0.05). The VHN values were significantly different among all groups in the following order: GS > FT > CL (p < 0.05). FT exhibited significantly higher microleakage scores compared to the CL and GS sealants (p < 0.05). The FR of FT was significantly greater than CL and GS (p < 0.05). Nano-filled resin based sealant can be used as an alternative to other fissure sealant materials because of its superior hardness results and feasible sealing ability.
Açıklama
Anahtar Kelimeler
Nano-filled fissure sealant, Conversion degree, Microhardness, Microleakage, Fluoride release
Kaynak
JOURNAL OF THE MECHANICAL BEHAVIOR OF BIOMEDICAL MATERIALS
WoS Q Değeri
Q1
Scopus Q Değeri
Q2
Cilt
3
Sayı
8
Künye
Ülker, M., Kuşgöz, A., Tüzüner, T., Kemer, B., Saray, O., (2010). Conversion Degree, Microhardness, Microleakage and Fluoride Release of Different Fissure Sealants. Journal of the Mechanical Behavior of Biomedical Materials, 3(8), 594-599. doi:10.1016/j.jmbbm.2010.07.00