Can Degradation of Adhesive Interfaces Due to Water Storage Affect Stress Distributions? A Finite-Element Stress Analysis Study
Küçük Resim Yok
Tarih
2016
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
QUINTESSENCE PUBLISHING CO INC
Erişim Hakkı
info:eu-repo/semantics/closedAccess
Özet
Purpose: The aim of this finite-element stress analysis (FEA) was to determine the effect of degradation due to water storage on stress distributions in root-filled premolar models restored with composite using either a self-etch (SE) or an etch-and-rinse (E&R) adhesive. Materials and Methods: Four premolar FEA models including root filling, MOD cavity, and composite restorations were created. The cavities were assumed to be treated by SE or E&R adhesives and stored in water for 18 months. The elastic properties of the adhesive-dentin interface after 24-h and 18-month water storage were obtained from the literature and applied to the FEA models. A 300-N load was applied on the functional cusps of the models. The SolidWorks/Cosmosworks structural analysis program was used and the results were presented considering the von Mises stresses. Results: Stresses in the cervical region increased over time on the load-application side of the main tooth models (SE: 84.11 MPa to 87.51 MPa; E&R: 100.24 MPa to 120.8 MPa). When the adhesive interfaces (hybrid layer, adhesive layer) and dentin were evaluated separately, the stresses near the root canal orifices increased over time in both models; however, this change was more noticeable in the E&R models. Stresses at the cavity corners decreased in the E&R model (within the adhesive layer), while SE models showed the opposite (within the hybrid layer). Conclusion: Change in the elastic modulus of the adhesive layer, hybrid layer, and dentin due to water storage has an effect on stresses in root-filled premolar models. The location and the level of the stresses differed depending on the adhesive used.
Açıklama
Anahtar Kelimeler
finite element analysis, dentin, elastic modulus, self-etch adhesive, etch-and-rinse adhesive, degradation
Kaynak
JOURNAL OF ADHESIVE DENTISTRY
WoS Q Değeri
Q2
Scopus Q Değeri
Q1
Cilt
18
Sayı
6